Evaluation of tooth color after bleaching with and without light-activation / Avaliação da coloração dental após clareamento com e sem ativação por luz

PURPOSE: The use of different light sources as an adjunct to in-office bleaching has been questioned. Thus, the aim of this study was to evaluate the color changes of teeth after application of bleaching techniques with different products, with and without activation by a LED-laser system. METHODS: Twenty-four bovine teeth surfaces were submitted to three bleaching techniques with two commercially available 35 percent hydrogen peroxide bleaching agents (n=8). The specimens were immersed in red wine for 48 h at 37°C and submitted to the bleaching techniques. Color changes were measured before and after staining as well as immediately after and 24 h after the bleaching treatments, with two different methods of color evaluation, software ScanWhite V1.1 and intra-oral spectrophotometer (Vita Easyshade). Data were analyzed by ANOVA and Kruskal-Wallis test. RESULTS: The statistical analysis showed that there was no statistically significant difference at 5 percent of significance level between the different groups, independently of the evaluation time, evaluation methods or the use of LED-laser systems. CONCLUSION: The results suggested that the use of light in the bleaching techniques did not influence the color changes.

OBJETIVO: o uso de diferentes fontes de luz como auxiliar no clareamento de consultório tem sido descrita na literatura.Assim, o objetivo deste estudo foi avaliar as alterações da cor dos dentes após a aplicação de técnicas de clareamento com diferentes produtos, com e sem ativação por um sistema de LED-laser. METODOLOGIA: Vinte-quatro superfícies de dentes bovinos foram submetidas a três técnicas de clareamento com dois agentes clareadores disponíveis comercialmente à base de peróxido de carbamida a 35 por cento (n=8). Os espécimes foram inicialmente imersos em vinho tinto por 48 ha 37°C, e submetidos às técnicas de clareamento. As alterações de cor foram mensuradas antes e após o manchamento, bem como imediatamente e 24 hs após as técnicas de clareamento, por meio de dois diferentes métodos de avaliação da cor: software ScanWhite V1.1 e espectrofotômetro intra-oral Vita Easyshade. Os dados foram analisados pelos testes de ANOVA e Kruskal-Wallis. RESULTADOS: A análise estatística não apontou diferenças significantes entre os diferentes grupos testados, independentemente do período de avaliação, método de avaliação ou uso do sistema LED-laser. CONCLUSÃO: Os resultados sugeriram que o uso da luz não influenciou nas mudanças de cor.

Avaliação da resistência à flexão de cerâmica dental Y-TZP: efeito de material e espessura / Evaluation of flexural strenght of Y-TZP dental ceramic: effect of material and thickness

O objetivo deste trabalho foi avaliar a resistência à flexão de cerâmicas de zircônia estabilizada por ítrio em função de marca comercial e espessura. A resistência à flexão (MPa) foi testada pelo método uniaxial de 3 pontos, conforme Norma ISO 6872/2005 em Máquina de Ensaios Universal EMIC DL 2000, usando célula de carga de 5kN, velocidade de 0,5 mm/min. e suporte com 20 mm de distância entre os apoios. Foram testados 2 sistemas cerâmicos de zircônia parcialmente estabilizada por ítrio (Y-TZP) ZirCAD© - Ivoclar Vivadente e LavaTM Framework - 3MESPE e 2 espessuras (norma ISO: 2,00 mm e uso clinico: 0,7 mm): ZC_2; ZC_0,7; LV_2 e LV_0,7. ANOVA one way e post Hoc de Bonferroni foram utilizados com significância para p<0,05. Não houve diferença estatisticamente significativa entre as médias de resistência a flexão entre ZC_2 (Média = 673,62 e dp = 129,95), ZC_0,7 (Média = 533,63 e dp = 129,84), LV_2 (Média = 593,56 e dp = 122,78) e LV_0,7 (Média = 673,02 e dp = 81,36). Conclusão: Os sistemas cerâmicos Y=TZP ZirCAD e Lava apresentam resistência a flexão (MPa) semelhantes independente da espessura. Espessuras de 0,7 mm podem ser utilizadas nos testes de resistência a flexão para melhor simular as situações de uso clinico dos sistemas cerâmicos Y-TZP

The objective of this study was to evaluate the flexural strength of ceramics by Yttrium stabilized zirconia as a function of thickness and trademark. Flexural strength (MPa) was tested by the method of three uniaxial points, in accordance with ISO 6872/2005. The Universal Testing Machine EMIC DL 2000, using a 5 kN load cell, crosshead speed of 0.5 mm / min. and holder with 20 mm distance between supports was used. We tested 2 systems ceramic zirconia partially stabilized by yttrium (Y-TZP) ZirCAD © - Ivoclar Vivadente and LavaTM Framework - 3MESPE and 2 thicknesses (ISO: 2.00 mm and clinical use: 0.7 mm): ZC_2; ZC_0 7; LV_2 and LV_0, 7. One-way ANOVA and post hoc Bonferroni was used with significance for p <0.05. There was no statistically significant difference between the mean flexural strength between ZC_2 (Mean = 673.62 and SD = 129.95), ZC_0, 7 (mean = 533.63 and SD = 129.84), LV_2 (Average = 593 , 56 and SD = 122.78) and LV_0, 7 (mean = 673.02 and SD = 81.36). Conclusion: Y-TZP ceramic systems ZirCAD and Lava have flexural strength (MPa) similar independent of the thickness. Thickness of 0.7 mm can be used in tests of flexural strength for better simulate the clinical conditions of use of Y-TZP ceramic systems